Celstran® PA66-GF50-02 P11
聚酰胺66
Ticona 

Technical Data

产品说明

Material code according to ISO 1043-1: PA66

Heat stabilized Nylon 66 reinforced by 50 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 11mm long.

Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.

The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding.

Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.

总体

材料状态 • 已商用：当前有效   
资料 1 •  Technical Datasheet (English)
  
  •  Processing - Injection (English)
  
     
Search for UL Yellow Card •  Ticona
  
 •  Celstran®
  
     
供货地区 • 北美洲 • 欧洲  
填料/增强材料 • 长玻璃纤维, 50% 填料按重量   
添加剂 • 热稳定剂   
性能特点 • 低翘曲性 • 高强度 • 热稳定性 
 • 刚性，高 • 耐低温撞击  
     
用途  • 金属置换   
RoHS 合规性 • 联系制造商   
加工方法 • 注射成型   
树脂ID (ISO 1043) • PA66   
    
物理性能  额定值 单位制 测试方法 
密度   1.56g/cm³ ISO 1183 
机械性能  额定值 单位制 测试方法 
拉伸模量  16400MPa ISO 527-2/1A/1 
拉伸应力 (断裂)  260MPa ISO 527-2/1A/5 
拉伸应变 (断裂)  2.2% ISO 527-2/1A/5 
弯曲模量 (23°C)  14900MPa ISO 178 
弯曲强度 (23°C)  425MPa ISO 178 
冲击性能  额定值 单位制 测试方法 
简支梁缺口冲击强度 (23°C)  40kJ/m² ISO 179/1eA 
热性能   额定值 单位制 测试方法 
熔融温度 3  260°C ISO 11357-3 

备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。

2 一般属性：这些不能被视为规格。

3 10°C/min