Celstran® PA66-GF40-02P11/15
聚酰胺66
Ticona ides.com/prospector
Technical Data

产品说明

Material code according to ISO 1043-1: PA66

Heat stabilized Nylon 66 reinforced by 40 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.

Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.

The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding.

Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment.

总体

材料状态 • 已商用：当前有效   
资料 1 •  Technical Datasheet (English)
  
  •  Processing - Injection (English)
  
     
Search for UL Yellow Card •  Ticona
  
 •  Celstran®
  
     
供货地区 • 欧洲   
填料/增强材料 • 长玻璃纤维, 40% 填料按重量   
添加剂 • 热稳定剂   
性能特点 • 低翘曲性 • 高强度 • 热稳定性 
 • 刚性，高 • 耐热性，高  
     
用途  • 金属置换   
RoHS 合规性 • 联系制造商   
加工方法 • 片材挤出成型 • 注射成型  
树脂ID (ISO 1043) • PA66   
    
物理性能  额定值 单位制 测试方法 
密度   1.46g/cm³ ISO 1183 
粘数   140cm³/g ISO 307 
机械性能  额定值 单位制 测试方法 
拉伸模量    
--   13700MPa ISO 527-2/1A/1 
80°C  9000MPa ISO 527-2 
拉伸应力    
断裂  180MPa ISO 527-2/1A/5 
80°C  130MPa ISO 527-2 
拉伸应变    
断裂  1.5% ISO 527-2/1A/5 
断裂, 80°C  2.0% ISO 527-2 
弯曲模量   ISO 178 
23°C  12600MPa  
80°C  8000MPa  
弯曲强度   ISO 178 
23°C  260MPa  
80°C  250MPa  

1 / 3

 
 
 
 
 
 
Celstran® PA66-GF40-02P11/15
聚酰胺66
Ticona   
      
  冲击性能 额定值 单位制 测试方法 
     
  简支梁缺口冲击强度  ISO 179/1eA 
  -30°C 23kJ/m²   
  23°C 23kJ/m²   
  简支梁缺口冲击强度  ISO 179/1eU 
  -30°C 41kJ/m²   
  23°C 40kJ/m²   
  悬壁梁缺口冲击强度  ISO 180/1A 
  -30°C 35kJ/m²   
  23°C 24kJ/m²   
  热性能 额定值 单位制 测试方法 
  热变形温度    
  1.8 MPa, 未退火 255°C ISO 75-2/A 
  8.0 MPa, 未退火 240°C ISO 75-2/C 
  熔融温度 3 261°C ISO 11357-3 
      
  注射 额定值 单位制   
  加工（熔体）温度 300 到 315°C   
  模具温度 90.0 到 120°C   
  注射说明    
  During the processing of CELSTRAN it is important to watch and    
  control melt shear, for excessive shear reduces fiber length and    
  mechanical performance as well.    
  Processing recommendation:    

• Conventional 3 zone screw, screw diameter minimum 40 mm
• Design flow channels for low melt shear
• Back pressure and screw rotation to realize a continous plastification performance and thus a homogeneous melt.

• Apply higher temperature settings than for short fiber compounds

备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。

2 一般属性：这些不能被视为规格。

3 10°C/min